ABSTRACT
Objective: To evaluate the effect of scaling procedures using different ultrasonic tips on the surface roughness, color stability and bacterial accumulation of lithium disilicate ceramic. Material and Methods: Scaling procedure was carried out using ultrasonic scaler (Satalec, Acteon, North America) with stainless-steel tip (US), titanium tip (UT) and plastic tip (UP), on disc shaped lithium disilicate samples cemented into a cavity prepared onto the labial surface of freshly extracted bovine teeth (10 samples per group). The samples were stored in coffee solution in an incubator at 37°C for 12 days, which is equivalent to 1 year of coffee consumption. The surface roughness was measured before and after the scaling procedure using a profilometer and atomic force microscopy. The color parameters were measured before and after scaling and staining procedures using VITA Easyshade Advance 4.0 according to the CIE L*a*b* color order system. The samples were then incubated with Streptococcus mutans (S. mutans) suspension. After incubation, the plates with 30 to 300 typical colonies of S. mutans were counted in a colony counter and mean values of colony forming units were obtained (CFU/mL). Results:The titanium scaling tip showed a statistically significant higher mean values of change in surface roughness ΔRa and bacterial count than the plastic scaling tip. Color changes (ΔE) were not a statistically significant among the groups. The results showed a statistically significant positive (direct) correlation between surface roughness and color change (p = 0.012) and also between surface roughness and bacterial count (p = 0.00). Conclusion: Within the limitations of this study, titanium scaling instruments cause irreversible surface alterations of lithium disilcate ceramics which was in direct correlation to the color changes and bacterial accumulation; therefore, dentists should proceed with caution when scaling lithium disilicate surfaces. The findings of the current study may indicate the need for instruments or equipment that can remove plaque and calculus without causing surface damage (AU)
Introdução: Avaliar o efeito de procedimentos de raspagem com diferentes pontas de ultrassom na rugosidade superficial, estabilidade de cor e acúmulo bacteriano em cerâmica de dissilicato de lítio. Material e Métodos: O procedimento de raspagem foi realizado usando um aparelho de ultrassom (Satalec, Acteon, América do Norte) com ponta de aço inoxidável (US), ponta de titânio (UT) e ponta de plástico (UP), em amostras de dissilicato de lítio em forma de disco cimentadas em uma cavidade preparada na superfície vestibular de dentes bovinos recém-extraídos (10 amostras por grupo). As amostras foram armazenadas em solução de café em incubadora a 37 ° C por 12 dias, o que equivale a 1 ano de consumo de café. A rugosidade da superfície foi medida antes e após o procedimento de raspagem usando um perfilômetro e um microscópio de força atômica. Os parâmetros de cor foram medidos antes e depois dos procedimentos de raspagem e armazenagem no café usando VITA Easyshade Advance 4.0 de acordo com o sistema de ordem de cores CIE L*a*b*. As amostras foram incubadas com suspensão de Streptococcus mutans (S. mutans). Após a incubação, as placas com 30 a 300 colônias típicas de S. mutans foram contadas em contador de colônias e obtidos os valores médios das unidades formadoras de colônias (UFC / mL). Resultados: A ponta de titânio mostrou valores estatisticamente maiores de mudança na rugosidade da superfície ΔRa e contagem de bactérias do que a ponta de raspagem de plástico. A mudança de cor (ΔE) não foi estatisticamente significativa entre os grupos. Os resultados mostraram uma correlação positiva (direta) estatisticamente significativa entre rugosidade superficial e alteração de cor (p = 0,012) e também entre rugosidade superficial e contagem bacteriana (p = 0,00). Conclusão: Dentro das limitações deste estudo, os instrumentos de raspagem de titânio causam alterações irreversíveis na superfície das cerâmicas de dissilicato de lítio que estão em correlação direta com as mudanças de cor e o acúmulo de bactérias. Portanto, os dentistas devem proceder com cautela ao realizar raspagem em superfícies de dissilicato de lítio. Os resultados deste estudo podem indicar a necessidade de instrumentos ou equipamentos que possam remover a placa e cálculo sem causar danos à superfície. (AU)
Subject(s)
Surface Properties , Ultrasonics , Bacterial Adhesion , Dental Scaling , ColorABSTRACT
Objective: TThe study evaluated in vitro the changes in roughness, color stability, and bacterial count of a CAD/CAM Resin Nano-Ceramic material surface treated by various scaling procedures. Material and Methods: 70 disks (5mm diameter, 0.5 mm thickness) of Resin Nano-Ceramic (Lava ™Ultimate, 3M, ESPE) material were cemented in standardized cavities prepared in bovine teeth. A custom-made scaling apparatus of a double pan balance was used for different scaling methods, simulating standard clinical conditions. The specimens were assigned to three main groups: no scaling(C), ultrasonic scaling (U), and manual scaling (M). Each group was then divided into three subgroups according to scaling tip material; stainless steel tip (St), plastic tip (P), and titanium tip (Ti). The surface texture was analyzed quantitatively and qualitatively with a tactile profilometer and atomic force microscopy. A spectrophotometer was used for color measurement. Streptococcus mutans were counted in a colony counter. All the data were tabulated and statistically analyzed. Results: Two-way ANOVA was used to study the effect while One-way ANOVA was performed to compare between study groups. The significance level was set at p ≤ 0.05. The ultrasonic titanium tip(UTi) revealed the significant highest mean value of alterations (p < 0.001). The integrity of the material surface was altered in the form of deep scratches on the ultrasonically scaled surfaces and numerous smaller scratches on the hand-scaled surfaces. Conclusion: The plastic instrument would appear to be the instrument of choice during a routine maintenance procedure for Resin Nano-Ceramic materials (AU).
Objetivo: Este estudo avaliou in vitro as alterações na rugosidade, estabilidade de cor e quantidade de bactérias da superfície de uma resina nano-cerâmica produzida em CAD/CAM tratada por diferentes procedimentos de raspagem. Material e Métodos: 70 discos (5 mm diâmetro, 0,5 espessura) de resina nano-cerâmica (Lava ™Ultimate, 3M, ESPE) foram cimentadas em cavidades padronizadas preparadas em dentes bovinos. Um aparato customizado de raspagem com pratos duplos de balança foram usados para os diferentes métodos de raspagem, simulando uma condição clínica padronizada. Os espécimes foram distribuídos em três principais grupos: Sem raspagem (C), raspagem ultrassônica (U) e raspagem manual (M). Cada grupo foi dividido em três subgrupos de acordo com a ponta do material de raspagem; ponta de aço inoxidável (St), ponta plástica (P), ponta de titânio (Ti). A textura da superfície foi analisada qualitativamente e quantitativamente por um perfilômetro tátil e microscopia de força atômica. Um espectrofotometro foi usado para a mensuração da cor. Estreptococos mutans foram contados em um contador de colônias. Todos os dados foram tabulados e analisados estatisticamente. Resultados: Anova dois fatores foi utilizado para estudar os efeitos, enquanto ANOVA um fator foi utilizado para comparar os grupos experimentais. O nível de significância foi estabelecido em p≤ 0,05. A ponta de ultrassom de titânio (UTi) revelou o valor significante mais alto de alterações (p < 0,001). A integridade da superfície d matérias foi alterada na forma ranhuras profundas, nas superfícies raspada por ultrassom e numerosas ranhuras menores nas superfícies raspadas à mão. Conclusão: O instrumento plástico poderia apresentar-se como um instrumento de escolha durante o pocedimento de manutenção routineira para materiais de resina nano-ceramica. (AU)
Subject(s)
Dental Scaling , Resin Cements , Dental PlaqueABSTRACT
Objective: Despite the higher translucency of nanocrystalline Y-TZP than the conventional Y-TZP, it couldn't be used in the anterior region of the mouth in its fully anatomical form without veneering for better esthetics. This study evaluated the color change (ΔE) and translucency parameter (TP) of the bilayered nano-crystalline zirconia restorations after different treatments of the zirconia surface before and after accelerated aging. Material and Methods: Forty samples of inCoris TZI were cut in the form of discs 15 mm (diameter) and 1mm (thickness) so that after sintering each disc dimensions' would be 12 mm (diameter) and 0.8 mm (thickness). All discs were colored by dipping in aqueous zirconia coloring solution of shade A2, then divided into four groups according to the type of surface treatment received before sintering; being tribochemical silica coating, zirconia powder deposition, glass grading, and a control untreated group. After sintering, all discs were veneered with a layer of porcelain 0.7 mm (thickness) and 12 mm (diameter). (ΔE) and TP were measured using VITA Easyshade Compact spectrophotometer before and after accelerated autoclave aging. Results: Different surface treatments applied had significant effect (P<0.05) over ΔE and TP. Glass graded group showed the highest ΔE value and the least TP value among both un-aged and aged sub-groups. Conclusion: Different surface treatments applied affected the color and translucency negatively where the control untreated group showed the highest TP and the least color deviation from the A2 color parameters. On the other hand, accelerated autoclave aging had no effect over translucency or color. (AU)
Objetivo: Apesar da maior translucidez da Y-TZP nanocristalina em relação à Y-TZP convencional, ela não pode ser usada na região anterior da boca em sua forma totalmente anatômica, sem o recobrimento cerâmico para uma melhor estética. Este estudo avaliou a mudança de cor (ΔE)eoparâmetrodetranslucidez(PT)das restauraçõesde zircônia nano-cristalina em duas camadas após diferentes tratamentos de superfície, antes e após o envelhecimento. Material e Métodos: Quarenta amostras de inCoris TZI foram cortadas na forma de discos de 15 mm (diâmetro) e 1 mm (espessura) para que, após sinterização, cada diâmetro dos discos fosse de 12 mm (diâmetro) e 0,8 mm (espessura). Todos os discos foram corados por imersão em solução aquosa de zircônia corante da sombra A2, divididos em quatro grupos de acordo com o tipo de tratamento de superfície recebido antes da sinterização; sendo revestimento de sílica químico-química, deposição de pó de zircônia, jateamento de vidro e um grupo de controle sem tratamento. Após a sinterização, todos os discos foram revestidos com uma camada de porcelana de 0,7 mm (espessura) e 12 mm (diâmetro). ΔE e TP foram medidos usando o espectrofotômetro VITA Easyshade Compact antes e depois do envelhecimento em autoclave. Resultados: Diferentes tratamentos de superfície aplicados tiveram efeito significativo (P <0,05) sobre ΔE o e maior TP. valor O grupo com de ∆E e o menor jateamento de vidro valor de TP apresentou entre os subgrupos não envelhecidos e envelhecidos. Conclusão: Diferentes tratamentos de superfície aplicados afetaram negativamente a cor e a translucidez, onde o grupo controle sem tratamento apresentou o maior TP e o menor desvio de cor dos parâmetros de coloração A2. Por outro lado, o envelhecimento acelerado da autoclave não teve efeito sobre a translucidez ou a cor. (AU)